how do you think flat glass is made. what if i told you they fucking pour molten glass onto molten tin at like 1000° so it floats & forms a perfectly flat layer & then slowly bring the temperature down until the glass has hardened enough to exit the tin bath.

that's crazy but what about pre-1960 before that method was industrialized?? oh, they would just literally blow that shit into a cylinder and cut it down the middle & reheat it until it became pliable before smoothing it out no big deal.

ok cool, any other ways? yeah sure, imagine a baker's dozen of non-lads (sorry but she specifies no lads even though some of the non-lads are clearly not pulling their weight...) dumping scoops of molten glass onto a plate where it's mixed with a fork before being smoothed out between two hollow water-cooled rolling pins.